Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 99.9%-99.95%;
Alloy: Non-alloy;
Type: Nickel Wire;
Powder: Not Powder;
Chemical Composition: Ni200 Ni201;
MOQ: 1kg;
Surface: Bright;
Density: 8.908 G/Cm³;
Resistance: 0.096;
Melting Point: 1435-1446;
Treatment: Hydrogen Annealing;
Elongation: 35%;
Ultimate Strength: 462MPa;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: ASTM;
Purity: 58%;
Alloy: Alloy;
Type: Hastelloy Wire;
Powder: Not Powder;
Chemical Composition: Ni Cr Mo Fe W Co;
Resistance: 1.5;
Ultimate Strength: 690MPa;
Elongation: 40%;
Melting Point: 1325-1370;
|
Application: Aviation, Electronics, Industrial, Chemical;
Standard: ASTM;
Purity: >99.99%;
Alloy: Non-alloy;
Type: Nickel Plate;
Powder: Not Powder;
Ultimate Strength (≥ MPa): 830;
Elongation (≥ %): 30;
Technique: Cold Treatment;
Surface: Bright;
MOQ: 10kg;
|
Application: Aviation, Electronics, Industrial, Chemical;
Standard: ASTM;
Purity: >99.99%;
Alloy: Non-alloy;
Type: Nickel Plate;
Powder: Not Powder;
Ultimate Strength (≥ MPa): 830;
Elongation (≥ %): 30;
Technique: Cold Treatment;
Surface: Bright;
MOQ: 10kg;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|