Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Color: White;
Chemical Composition: Al2O3 Sio2;
Density (Kg/M³): 280~500;
Thickness: 3~50mm;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Square, Circular, Triangular, etc;
Material: Mullite, Cordierite, High Alumina, etc;
Size: 50*50, 40*40, 65*65, 50*75, etc;
Hole Shape: Square, Circular, Triangular, Hexagonal, etc;
Holes: 20, 30, 40, etc;
Usage: Metallurgy Casting;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Magnesium Oxide Boards;
Shape: Plate;
Material: MGO Board;
Color: White, Grey, Red, Green;
Density: 1.0-1.2g/cm3(GB/T-7019-1997);
Fire Ratings: A1 Grade (GB 8624);
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Magnesium Oxide Boards;
Shape: Plate;
Material: MGO Board;
Color: White, Grey, Red, Green;
Density: 1.0-1.2g/cm3(GB/T-7019-1997);
Fire Ratings: A1 Grade (GB 8624);
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Magnesium Oxide Boards;
Shape: Square;
Material: MGO Board;
Color: White, Grey, Red, Green;
Density: 1.0-1.2g/cm3(GB/T-7019-1997);
Fire Ratings: A1 Grade (GB 8624);
|