Specification |
Refractoriness (℃): 1400-1500;
Feature: Instant Materials;
Type: Refractory Material;
Shape: Crescent;
Material: Metalwork;
Melting PointºC: 1425-1510;
Spring Module at 876ºC 104MPa: 8.27;
MPa Tensile Strength at 870ºC: 48;
Heat-Shrinking Coefficient at 870º: 13.68;
Heat-Conductibility at 500ºC W/M.K: 26.3;
Proportion at Room Temp., g/cm3: 7.8;
Weight Loss After Circular Oxidation Abo: 70;
Erosion in The H2s,Mil/Yr: 200;
Max Working Temp. in The So2 ,ºC: 800;
Erosion in The Natural Gas at 815º: 12;
Erosion in The Coal Gas From The Cookery: 236;
Nitrification in The Anhydrous Ammonia a: 80-175;
Erosion in The H2,at 454ºC,Mil/Yr: 21.9;
Carbon Content of The Alloy After Solid: 1.03;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace,Glass Furnace,Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Block;
Material: Alumina Block;
Product Number: Azs Refractory Brick;
Brand Name: Rongsheng;
Zro2 Content(%): ≥40;
Na2o Content(%): ≤1.3;
Fe2o3+TiO2 Content(%): ≤0.3;
Bulk Density(g/cm3): ≤3.9;
Density: ≤3.8;
Application: Glass Kiln;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace,Glass Furnace,Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Instant Materials;
Type: Refractory Material;
Shape: Block;
Material: Alumina Block;
|