Specification |
CAS No.: No;
Formula: CH2=Chcooch2CH2oconhr1nhcoor2ocoor1nhcooch2CH2ococ;
EINECS: No;
Molecular Principal Chain: Carbon Chain Polymer;
Color: Transparent;
Product Name: Polyurethane Acrylate;
Style: Oligomer;
Funtional Group: 2 Funtional;
Application: 3c Coating,Ink Printing;
Advantage: Good Yellow Resistance;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 79-89;
Density,g/cm3: 1.2-121;
Tensile Strength,MPa: 24-30;
Tear Strength,MPa: 75-90;
Elongation at Break,%: 600-800;
Tg ,ºC: -18~-36;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 83-96;
Density,g/cm3: 1.07-1.14;
100% Modulus,MPa: 5-10;
300% Modulus,MPa: 10-25;
Tensile Strength,MPa: 30-45;
Tear Strength,MPa: 77-120;
Procesing Temperature,°c: 165-180;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 63-86;
Density,g/cm3: 1.06-1.12;
100% Modulus,MPa: 2.5-6;
300% Modulus,MPa: 4-10;
Tensile Strength,MPa: 9-20;
Tear Strength,MPa: 35-75;
Elongation at Break,%: 700-950;
Tear Strength,Kn/M: 35-75;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 75-97;
Density,g/cm3: 1.2;
Tensile Strength,MPa: 15-35;
Elongation at Break,%: 450-700;
Tack Free Time,Min: 2-10;
|