Specification |
CAS No.: 25067-11-2;
Formula: {[C2f4]N[CF3]}M;
Molecular Principal Chain: High-Molecular Polymer;
Color: Translucent;
Tensile Breaking Strength: >26MPa;
Elongation at Break: >300%;
Relative Density: 2.12-2.17g/cm3;
Dielectric Constant(106Hz ): ≤2.1;
Application: Insulation Jacket of Wire;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Density g/cm3: 1.25;
100% Modulus MPa: 16.0;
Tensile Strength MPa: 40.0;
Elongation at Break: 450 %;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 95;
Density,g/cm3: 1.24;
100% Modulus,MPa: 13;
300% Modulus,MPa: 25;
Tensile Strength,MPa: 25;
Tear Strength,N/mm: 140;
Elongation at Break,%: 500;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 97;
Density,g/cm3: 1.24;
100% Modulus,MPa: 18;
300% Modulus,MPa: 30;
Tear Strength,N/mm: 185;
Elongation at Break,%: 500;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 95;
Density,g/cm3: 1.24;
100% Modulus,MPa: 15;
300% Modulus,MPa: 26;
Tensile Strength,MPa: 40;
Tear Strength,Map: 40;
Elongation at Break,,%: 500;
|