Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Al2O3: at Least 80%;
Zro2: at Least 3%;
Cr2o3: at Least 12%;
Bulk Density: at Least 2.9 g/cm3;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Block;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 18-20%;
Bulk Density: 2.75-3.1g/cm3;
Cold Crushing Strength: 70-90MPa;
Refractoriness Under Load: 1650-1700ºC;
Al2O3: 85-98.5%;
Fe2o3: 0.2-0.5%;
Sio2: 0.3-18%;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Block;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 18-20%;
Bulk Density: 2.75-3.1g/cm3;
Cold Crushing Strength: 70-90MPa;
Refractoriness Under Load: 1650-1700ºC;
Al2O3: 85-98.5%;
Fe2o3: 0.2-0.5%;
Sio2: 0.3-18%;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Block;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 18-20%;
Bulk Density: 2.75-3.1g/cm3;
Cold Crushing Strength: 70-90MPa;
Refractoriness Under Load: 1650-1700ºC;
Al2O3: 85-98.5%;
Fe2o3: 0.2-0.5%;
Sio2: 0.3-18%;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Block;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 18-20%;
Bulk Density: 2.75-3.1g/cm3;
Cold Crushing Strength: 70-90MPa;
Refractoriness Under Load: 1650-1700ºC;
Al2O3: 85-98.5%;
Fe2o3: 0.2-0.5%;
Sio2: 0.3-18%;
|