Specification |
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Chromium Carbide;
Type: Wear Resistant Pipe;
Hardness: HRC58-63;
Chromium Content: 22-32%;
Grade: Q235/Q345+Chrome Carbide;
Delivery Time: 8-14 Days;
Use: Mining ;Power Utility;Steel Mill;Coal ;Cement;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Plate;
Color: White;
MOQ: 50kg;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|