Specification |
Technique: Washed Kaolin;
Application: Paper, Ceramic, Refractory;
Shape: Powder;
Fe2o3 Content (%): <=0.5;
Moisture Content (%): <=0.5;
K2o Content (%): <0.3;
Sio2 Content (%): 52+-2;
Al2O3 Content (%): 45+-2;
TiO2 Content (%): <=1.5;
Appearance: White Powders;
|
Technique: Washed Kaolin;
Application: Ceramic;
Shape: Powder;
Usage: Ceramic,Industrial,Plastic,Ink,Coating;
Fe2o3 Content (%): About1.6;
TiO2 Content (%): Min0.6%;
L.O.I: About45;
Whiteness: Min0.2%;
Brand: Min0.2%;
K2o Content (%): Max44;
Oil Absorption(G/Ml): About7;
Al2O3 Content (%): Min54%;
pH: Min54%;
Sio2 Content (%): Max94;
Moisture Content (%): 1.5max;
|
Technique: Washed Kaolin;
Application: Ceramic;
Shape: Powder;
Usage: Ceramic,Industrial,Plastic,Ink,Coating;
Fe2o3 Content (%): About1.6;
TiO2 Content (%): Min0.6%;
L.O.I: About45;
Whiteness: Min0.2%;
Brand: Min0.2%;
K2o Content (%): Max44;
Oil Absorption(G/Ml): About7;
Al2O3 Content (%): Min54%;
pH: Min54%;
Sio2 Content (%): Max94;
Moisture Content (%): 1.5max;
|
Technique: Washed Kaolin;
Application: Ceramic;
Shape: Powder;
Usage: Ceramic,Industrial,Plastic,Ink,Coating;
Fe2o3 Content (%): About1.6;
TiO2 Content (%): Min0.6%;
L.O.I: About45;
Whiteness: Min0.2%;
Brand: Min0.2%;
K2o Content (%): Max44;
Oil Absorption(G/Ml): About7;
Al2O3 Content (%): Min54%;
pH: Min54%;
Sio2 Content (%): Max94;
Moisture Content (%): 1.5max;
|
Technique: Washed Kaolin;
Application: Refractory;
Shape: White Power;
Type: Powder;
Fe2o3 Content (%): 0.3max;
Al2O3 Content (%): 38+2.0;
TiO2 Content (%): 0.6max;
Sio2 Content (%): About47;
Moisture Content (%): 1.0max;
Weight: 25kg;
|