Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia Chrome;
MGO: >50%;
Cr2o3: 12-20%;
Bulk Density: >3.05g/cm3;
Apparent Porosity: 15-17%;
Cold Crushing Sternth: 60-80MPa;
|
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Long Time Materials, Instant Materials, Long Time Materials, Instant Materials;
Material: Soda Lime Borosilicate Glass, Soda Lime Borosilicate Glass;
Shotblast Type: Shot Blasting;
Sandblasting Type: Automatic Sandblasting;
Shotblast Application: Guns and Tanks;
Sandblasting Method: Dry Spray;
Sandblasting Applications: Metallurgy;
Shotblast Material: Glass;
Appearance: Transparent;
Density: 2.4-2.6g/cm3;
Hardness: 6-7moh's;
Roundness: >80%;
Sio2: >72%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Sand/Particles/Powder;
Material: Alumina Block;
Calcined Kiln Styles: Shaft Kiln, Rotary Kiln, Round Kiln;
Standard: Yb/T 5179-93;
Application: Refractories;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Sand/Particles/Powder;
Material: Alumina Block;
Calcined Kiln Styles: Shaft Kiln, Rotary Kiln, Round Kiln;
Standard: Yb/T 5179-93;
Application: Refractories/Fire Bricks;
Package: 1mt/1.25mt/1.35mt Per Jumbo Bag;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Sand/Particles/Powder;
Material: Alumina Block;
Calcined Kiln Styles: Shaft Kiln, Rotary Kiln, Round Kiln;
Standard: Yb/T 5179-93;
Application: Refractories/Fire Bricks;
Package: 1mt/1.25mt/1.35mt Per Jumbo Bag;
|