Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Refractory Materials;
Type: Refractory Material;
Shape: Brick;
Material: MgO-Carbon Brick;
Brand: Hitech;
Bulk Density: ≤ 2.90 g/cm3;
Apparent Porosity: ≤16%;
Cold Crushing Strength: ≥60MPa;
Application: Slag Line;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Hot Sale;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Product Name: Silica Bricks;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Application: Metallurgy;
Standard Size: 230X114X65;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Hot Sale;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Product Name: Silica Bricks;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Application: Metallurgy;
Standard Size: 230X114X65;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Hot Sale;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Product Name: Silica Bricks;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Application: Metallurgy;
Standard Size: 230X114X65;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Hot Sale;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Product Name: Silica Bricks;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Application: Metallurgy;
Standard Size: 230X114X65;
|