Specification |
Feature: Insulation Material;
Refractoriness (℃): 1100~1350ºC;
Shape: Plate;
Al2O3: 44%;
Sio2: 52%;
Fe2o3: 1%;
Density: 260/320kg/M3;
Specification Tem: 1260ºC;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability, Long Time Materials;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability, Long Time Materials;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability, Long Time Materials;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability, Long Time Materials;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|