Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Mullite;
Al2O3 (%): 70~85%;
Fe2o3 (%): 1.2~0.5%;
Sio2 (%): 26~13%;
Bulk Density g/cm3: 2.50~2.95;
Apparent Porosity: 17%;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition: Al2O3.Sio2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260c, 1430c;
Certifiacte: ISO9001, CE, etc;
Shot Content (%): 12-15;
Al2O3: 34-44;
Sio2: 50-52;
Fiber Diameter(μm): 3.5;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition: Al2O3.Sio2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260c, 1430c;
Certifiacte: ISO9001, CE, etc;
Shot Content (%): 12-15;
Al2O3: 34-44;
Sio2: 50-52;
Fiber Diameter(μm): 3.5;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition: Al2O3.Sio2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260c, 1430c;
Certifiacte: ISO9001, CE, etc;
Shot Content (%): 12-15;
Al2O3: 34-44;
Sio2: 50-52;
Fiber Diameter(μm): 3.5;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition: Al2O3.Sio2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260c, 1430c;
Certifiacte: ISO9001, CE, etc;
Shot Content (%): 12-15;
Al2O3: 34-44;
Sio2: 50-52;
Fiber Diameter(μm): 3.5;
|