Specification |
CAS No.: 25135-73-3;
Formula: /;
EINECS: /;
Molecular Principal Chain: /;
Color: Transparent;
Viscosity(P/200ºC): 95-125;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: -/80~~-/85;
Density,g/cm3: 1.20;
Tensile Strength,MPa: 70-95;
Tear Strength,MPa: 200-220;
Elongation at Break,%: 25-150;
Tg,°c: 90-130;
Flexural Strength,MPa: 115-120;
Flexural Modulus,MPa: 2150-2200;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
Tensile Strength,MPa: 38-60;
Tear Strength,MPa: 110-220;
Elongation at Break,%: 300-550;
Tg,°c: -42~-30;
100% Modulus,MPa: 5-34;
300% Modulus,MPa: 10-45;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: -/80~~-/85;
Density,g/cm3: 1.20;
Tensile Strength,MPa: 70-95;
Tear Strength,MPa: 200-220;
Elongation at Break,%: 25-150;
Tg,°c: 90-130;
Flexural Strength,MPa: 115-120;
Flexural Modulus,MPa: 2150-2200;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
Tensile Strength,MPa: 38-60;
Tear Strength,MPa: 110-220;
Elongation at Break,%: 300-550;
Tg,°c: -42~-30;
100% Modulus,MPa: 5-34;
300% Modulus,MPa: 10-45;
|