Specification |
CAS No.: 28774-87-0;
Formula: (C20h38n2o2)N;
Molecular Principal Chain: Carbon Chain Polymer;
Color: Translucence;
Type: Polyamide PA Nylon Granules;
Certificates: SGS;
Material: 100% Nylon;
Grade: Injection Grade;
Application: Building, Automotive, Electronic, Household;
Item: Nylon Raw Material;
Molding Method: Injection;
Usage: Engineering Plastics, Copolymerized Nylon;
Supply Ability: 800 Metric Tons Per Month;
Physical Properties: High Chemical Resistance High Mechanical Strength;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
Tensile Strength,MPa: 38-60;
Tear Strength,MPa: 110-220;
Elongation at Break,%: 300-550;
Tg,°c: -42~-30;
100% Modulus,MPa: 5-34;
300% Modulus,MPa: 10-45;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: -/80~~-/85;
Density,g/cm3: 1.20;
Tensile Strength,MPa: 70-95;
Tear Strength,MPa: 200-220;
Elongation at Break,%: 25-150;
Tg,°c: 90-130;
Flexural Strength,MPa: 115-120;
Flexural Modulus,MPa: 2150-2200;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
Tensile Strength,MPa: 38-60;
Tear Strength,MPa: 110-220;
Elongation at Break,%: 300-550;
Tg,°c: -42~-30;
100% Modulus,MPa: 5-34;
300% Modulus,MPa: 10-45;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
Tensile Strength,MPa: 38-60;
Tear Strength,MPa: 110-220;
Elongation at Break,%: 300-550;
Tg,°c: -42~-30;
100% Modulus,MPa: 5-34;
300% Modulus,MPa: 10-45;
|