Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Chemical Composition: Ni 76%;
Characteristics: High Resistivity, Good Anti-Oxidation Resistance;
Range of Application: Resistor, Heater,Chemical;
Electrical Resistivity: 1.09 Ohm mm2/M;
The Highest Use Temperature: 1400;
Density: 8.4G/Cm3;
Elongation: >=20%;
Hardness: 180 Hv;
Max Working Temperature: 1200;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|