Specification |
Refractoriness (℃): 1260c, 1350c, 1430c;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Blanket;
Material: Al2O3+Sio2;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Zro2;
Al2O3: Min40-44%;
Application: Glass Furnace;
Brick: Azs;
Refractory Material: Fireproof Material;
High Alumina Brick: Corundum Brick;
Zro2: 33%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Powder;
Material: Alumina Cement;
Al2O3 Content: 80,83,85,88,90;
Density: 2.9,3.15,3.2,3.3;
Water Absorption: 7,6,5,4;
Usage: High Alumina , Cement Refractory;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace,Glass Furnace,Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace,Glass Furnace,Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
|