Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Needle;
Kind: Low Temperature Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃, 1350ºC;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Temperature: 1260c, 1350c, 1430c;
Certifiacte: ISO9001:2000;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃, 1350ºC;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Temperature: 1260c, 1350c, 1430c;
Certifiacte: ISO9001:2000;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Paper;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fiber Paper;
Product Name 2: Ceramic Fiber Blanket;
Working Temperature: 1100-1350 Degree;
Compression Strength(MPa): 0.5;
Color: Pure White;
Chemical Composition: Al2O3 and Sio2;
Density: 280-500G/M3;
Product Advantage: Low Thermal Conductivity;
Application: Industrial Thermal Insulation;
Application 2: Corrosion Resistance Material;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Fireproof Insulation Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|