Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Vacuum Forming;
Kind: Refractory Material;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050~1600 C.Degree;
Chemical Composition:: Al2O3+Sio2≥99%;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Ceramic Fiber Bulk Wool;
Kind: Ordinary Ceramic Fiber;
Thickness: 6mm-50mm, 1", 1/2"2";
Ultimate Strength (≥ MPa): 0.5MPa (25mm Thickness);
Fiber Diameter: 3-5μm;
Thermal Conductivity: 0.06-0.12;
Classification Temperature: 1200;
Ttensile Strenghth(_Kpa): 30/50/70;
Width: 100mm-1220mm;
Shrinkage (1800 ºF, 3h): 1050~1600 C.Degree;
Density (Kg/M³ ): 128;
Al2O3: ≥43;
Zro2: ≥54;
Permanent Linear Shrinkage: 1000c*24HS2.5;
Density: 64/96/128;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Sio2+Cao;
Shape: Board;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition:: Al2O3.SiO2, Al2O3+Sio2+Zro2;
Shape: Ceramic Fiber Module;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1350/1430;
Certifiacte: ISO9001, CE, etc;
Linear Shrinkage After Heating: 1000ºC*24h<=2.5-3.5;
Bulk Density(g/cm3): 180-240;
Thermal Conductivity: 0.09-0.175;
Al2O3: 34-45%;
Sio2: 50-54%;
Zro2: 15%;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Sio2+Cao;
Shape: Board;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|