Specification |
CAS No.: 21645-51-2;
Formula: Al(Oh)3;
EINECS: 244-492-7;
Classification: Alkaline,Aluminum Hydroxide;
Grade Standard: Industrial Grade;
Kind: Alkaline Oxide;
Quality: First Class;
Ath Model: H-Wf-/14/25/25msp/50/75/90;
Particle Size Um: 1-10um,14-100 Um Customized;
Whiteness >: 92-95grade 97-99grade;
Al(Oh)3 % >: 99.6;
Sio2 %<: 0.01;
Fe2o3 %<: 0.008;
Na2o %: 0.3;
Moisture %: 0.2;
Absorption (Ml/100g): 21-35;
1: Filler for Artificial Marble Stone;
2: Filler for Acrylic Solid Surface;
3: Filler for SMC(Sheet Molded Plastic), BMC;
4: Filler for Artificial Onyx/Panel/Agate;
5: Flame Retardant Powder for Cable;
6: Aluminum Hydroxide for PVC Compound;
|
CAS No.: 1314-23-4;
Formula: Zro2;
EINECS: 215-227-2;
Classification: Other Oxides;
Grade Standard: Industrial Grade;
Kind: Acidic Oxide;
Quality: First Class;
Application: Ceramic, Battery, Refractory Products;
Melting Point: 2700°c;
Particle Size: 20nm, 30-50nm, 80-100nm, 200-400nm, 1.5-150um;
Density: 5.85 G/Cm³;
Boiling Point: 4300 ºC;
Product Name: Zirconium Oxide Powder;
Appearance: White Odorless and Tasteless Crystals;
|
CAS No.: 21645-51-2;
Formula: Al(Oh)3;
EINECS: 244-492-7;
Classification: Alumina;
Grade Standard: Industrial Grade;
Kind: Alkaline Oxide;
Quality: First Class;
Al(Oh)3 Content: 99.5%Min;
Appearance: White Powder;
Whiteness: 93%/95%/98%;
Application: Filler of Solid Surface, Flame Retardant;
Keywords: Alumina Trihydrate/Ath/Aluminium Hydrate Powder;
MOQ: 1 Ton or Small Quantity;
Sample: Free Sample;
|
CAS No.: 13463-67-7;
Formula: TiO2;
EINECS: 236-675-5;
Classification: Titanium Dioxide;
Grade Standard: Industrial Grade;
Kind: Acidic Oxide;
Quality: Eligible;
Molecular Weight: 79.8658;
Melting Point: 1560 ~ 1580ºC;
Hazard Class Code: R20;
Shape: Powder;
|
CAS No.: 13463-67-7;
Formula: TiO2;
EINECS: 236-675-5;
Classification: Titanium Dioxide;
Grade Standard: Industrial Grade;
Kind: Amphoteric Oxide;
Quality: First Class;
Inorganic Surface Treatment: Ai2o3,Zro2;
TiO2 Content %: >=93;
Brightness %: 94.5;
Organic Surface Treatment: Yes;
Volatile Matters at 105c ,%: <=0.5;
pH Value of Water Suspension: 6.5~8.5;
Oil Absorption Value (G/100g): <=17;
Tint Reducing Power, Ryenolds Number, Tc: >=1800;
Electrical Resistance of Aqueous Extract: >=80;
Water Soluble Matters,%: <=0.5;
Residue on Sieve (45 Um Mesh), %: >=0.02;
Oil Dispersible Power (Hegemann Number): <=6.0;
Rutile Content, %: <=97.0;
Whiteness,( Compared with Standard Sampl: No Less Than;
|