Specification |
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Ceramic Fiber Paper, Roll;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400C, 1260C;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1000/1100/1300;
Certifiacte: ISO9001, CE, etc;
Width: 610mm 1220mm;
Bulk Density(g/cm3): 200;
Thickness: 0.5-10mm;
Al2O3: 40-48;
Sio2: 51-52;
Tensile Strength: 0.4;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Process;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80%;
Fe2o3: 1.5-2.5%;
Bulk Density: 2.25-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55/Ha65/Ha70/Ha75/Ha80;
Refractoriness Under Load (0.2MPa): 1450-1700 ºC;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Process;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80%;
Fe2o3: 1.5-2.5%;
Bulk Density: 2.25-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55/Ha65/Ha70/Ha75/Ha80;
Refractoriness Under Load (0.2MPa): 1450-1700 ºC;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Process;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80%;
Fe2o3: 1.5-2.5%;
Bulk Density: 2.25-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55/Ha65/Ha70/Ha75/Ha80;
Refractoriness Under Load (0.2MPa): 1450-1700 ºC;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Process;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80%;
Fe2o3: 1.5-2.5%;
Bulk Density: 2.25-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55/Ha65/Ha70/Ha75/Ha80;
Refractoriness Under Load (0.2MPa): 1450-1700 ºC;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|