Specification |
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Ceramic Fiber Paper, Roll;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400C, 1260C;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1000/1100/1300;
Certifiacte: ISO9001, CE, etc;
Width: 610mm 1220mm;
Bulk Density(g/cm3): 200;
Thickness: 0.5-10mm;
Al2O3: 40-48;
Sio2: 51-52;
Tensile Strength: 0.4;
|
Calcination Temperature: 1720 Degree;
Price Clause: Fob Crf CIF Are Accepted;
Delivery Date: 7-12 Days After Contract Signing;
Vessle Type: by Containers or by Bulk Vessle Are Accepted;
|
Calcination Temperature: 1720 Degree;
Price Clause: Fob Crf CIF Are Accepted;
Delivery Date: 7-12 Days After Contract Signing;
Vessle Type: by Containers or by Bulk Vessle Are Accepted;
|
Classification: High-Alumina;
Feature: High-Temperature Resistant;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Grit / Grain/ Powder;
Advantage: 20 Years' Manufacturer,QC and Lead Time Guaranteed;
Al2O3: 85% Min;
Fe2o3: 2% Max;
Sio2: 8% Max;
TiO2: 4% Max;
K2o+Na2o: 0.3% Max;
Cao+MGO: 0.5% Max;
Bulk Density: 3.20 Min;
Customize: Yes, Technical Data Sheet Needed;
Certificates: ISO9001/ISO14001/ISO18001;
|
Classification: High-Alumina;
Feature: High-Temperature Resistant;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Grit / Grain/ Powder;
Advantage: 20 Years' Manufacturer,QC and Lead Time Guaranteed;
Al2O3: 85% Min;
Fe2o3: 2% Max;
Sio2: 8% Max;
TiO2: 4% Max;
K2o+Na2o: 0.3% Max;
Cao+MGO: 0.5% Max;
Bulk Density: 3.20 Min;
Customize: Yes, Technical Data Sheet Needed;
Certificates: ISO9001/ISO14001/ISO18001;
|