Specification |
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Roll, Ceramic Fiber Blanket;
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1100;
Bulk Density(g/cm3): 64-128;
Linear Shrinkage After Heating: -2.5;
Tensile Strength(MPa): 0.03-0.05;
Sio2: 55-65%;
Cao: 22-35%;
MGO: 5-10%;
Fiber Diameter: 3.5um;
Shot Content: 12%;
|
Classification: High-Alumina;
Feature: High-Temperature Resistant;
Production Process: Casting Method;
Refractoriness (℃): Refractoriness> 2000;
Shape: Grit / Powder/ Grain;
Grit 1: 0-1mm, 1-3mm, 3-5mm, 5-8mm, 8-15mm;
Grit 2: 0-200 Mesh, 0-325 Mesh;
Chemical Al2O3: 75%, 80%, 85%, 86%, 87%, 88%, 90%,;
Advantage: Manufacturer;
|
Classification: High-Alumina;
Feature: High-Temperature Resistant;
Production Process: Casting Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Grit / Powder/ Grain;
Al203 Content: 80-88%;
Hardness: 1-3;
Bulk Density: 1.2-1.3;
Color: Yellow,Blue;
|
Classification: High-Alumina;
Feature: High-Temperature Resistant;
Production Process: Casting Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Grit / Powder/ Grain;
Al203 Content: 80-88%;
Hardness: 1-3;
Bulk Density: 1.2-1.3;
Color: Yellow,Blue;
|
Classification: High-Alumina;
Feature: High-Temperature Resistant;
Production Process: Casting Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Grit / Powder/ Grain;
Al203 Content: 80-88%;
Hardness: 1-3;
Bulk Density: 1.2-1.3;
Color: Yellow,Blue;
|