Specification |
Material: Acrylic;
Kind: Transparent Plastic Sheet;
Water Absorption: 0.2%~0.4%;
Contraction Percentage: <0.4%;
Tensile Strength: 51~80MPa;
Raw Material: 100% Virgin MMA;
Transparency: 93%;
Quality: UV Light Resistance;
Density: 1.2g/Cm³;
Thickness: 1.8m~50mm;
Protective Film: PE Film or Brown Craft Paper, Customized Available;
MOQ: 300 Kg;
Certificates: CE, SGS, ISO;
Samples: Free;
Loading Port: Shanghai/Ningbo;
|
Material: PE;
Kind: Engineering Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 81~130MPa;
Thickness: 6-260mm;
Thickness Tolerance: +0.5mm;
Application: Marine Fender Pad, Outrigger Pad, Engineering Part;
UV Stable: Yes;
Test Certification: SGS, Ce, TUV, ISO;
Weight: 10-300kgs;
Density: 0.94-0.96;
Quality Guarantee: 3 Years;
Molecular Weight: 0.5-9 Million;
|
Material: PE;
Kind: Engineering Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 81~130MPa;
Thickness: 6-260mm;
Thickness Tolerance: +0.5mm;
Application: Marine Fender Pad, Outrigger Pad, Engineering Part;
UV Stable: Yes;
Test Certification: SGS, Ce, TUV, ISO;
Weight: 10-300kgs;
Density: 0.94-0.96;
Quality Guarantee: 3 Years;
Molecular Weight: 0.5-9 Million;
|
Material: PE;
Kind: Engineering Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 81~130MPa;
Thickness: 6-260mm;
Thickness Tolerance: +0.5mm;
Application: Marine Fender Pad, Outrigger Pad, Engineering Part;
UV Stable: Yes;
Test Certification: SGS, Ce, TUV, ISO;
Weight: 10-300kgs;
Density: 0.94-0.96;
Quality Guarantee: 3 Years;
Molecular Weight: 0.5-9 Million;
|
Material: PE;
Kind: Engineering Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 81~130MPa;
Thickness: 6-260mm;
Thickness Tolerance: +0.5mm;
Application: Marine Fender Pad, Outrigger Pad, Engineering Part;
UV Stable: Yes;
Test Certification: SGS, Ce, TUV, ISO;
Weight: 10-300kgs;
Density: 0.94-0.96;
Quality Guarantee: 3 Years;
Molecular Weight: 0.5-9 Million;
|