Specification |
CAS No.: 25035-69-2;
EINECS: C15h14o8;
Molecular Principal Chain: Heterochain Polymer;
Color: White;
Appearance: Transparent Mucus, No Mechanical Impurities;
Chroma(Fe-Co): ≤1#;
Viscosity at 25ºC: Z2-Z4;
Solid Content: 50±1;
Acid Value: ≤8;
Tg: 50;
Solvent: Tol,Xyl;
Package: 220 Kg/Barrel;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
Tensile Strength,MPa: 38-60;
Tear Strength,MPa: 110-220;
Elongation at Break,%: 300-550;
Tg,°c: -42~-30;
100% Modulus,MPa: 5-34;
300% Modulus,MPa: 10-45;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
Tensile Strength,MPa: 38-60;
Tear Strength,MPa: 110-220;
Elongation at Break,%: 300-550;
Tg,°c: -42~-30;
100% Modulus,MPa: 5-34;
300% Modulus,MPa: 10-45;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 75-97;
Density,g/cm3: 1.2;
Tensile Strength,MPa: 15-35;
Elongation at Break,%: 450-700;
Tack Free Time,Min: 2-10;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 43-50;
Density,g/cm3: 0.2-0.23;
Tensile Strength,MPa: 1.3;
Elongation at Break,%: 170;
Tear Strength,Kn/M: 15;
Rebounding,%: 58;
Compression Set(50% 6h, 45ºC),%: 10-15;
|