Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3: Min65%;
Application: Industrial Blast Furnace;
Brick: High Alumina Brick;
Refractory Material: Fireproof Material;
Fire Brick: Corundum Brick;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35,Sk36,Sk37,Sk38,Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Block;
Material: Zro2;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 1.3-2.0%;
Bulk Density: 3.4-4.0g/cm3;
Cold Crushing Strength: 350MPa;
Thermal Linear Expansion(%): 0.8;
Zro2: 32-40%;
Na2o: 1.3-1.5%;
Sio2: 13-15.5%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Block;
Material: Zro2;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 1.3-2.0%;
Bulk Density: 3.4-4.0g/cm3;
Cold Crushing Strength: 350MPa;
Thermal Linear Expansion(%): 0.8;
Zro2: 32-40%;
Na2o: 1.3-1.5%;
Sio2: 13-15.5%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 0.6-1.25;
Cold Crushing Strength: 1.0-10MPa;
Thermal Conductivity: 0.17-0.51;
|