Specification |
Type: Graphite Mold;
Composition: 99.9% High Purity Graphite;
Carbon Content: High-Carbon;
Grade: High Purity Graphite;
Forming Way: Molded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Density: 1.70-1.92g/cm3;
Resistivity: Less Than 12;
Compressive Strength: More Than 70MPa;
Porosity: Less Than 26%;
Elasticity Modulus  : 6-18gpa;
Thermal Expansion Coefficient: 1.47-4.25;
Temperature Resistance  : Less Than 4350 Degree;
Ash Content: Less Than 0.05%;
|
Type: Flake Graphite;
Composition: C;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Expanded Graphite;
Crystal Morphology: Flake Graphite;
Melting Point: 3250 Degree;
pH: 6-7;
Ash: 5-10%;
80 Mesh: Over 75%;
Color: Black, Sliver Grey;
Fixed Carbon: 90-99%;
Expandable Rate: 180ml/G - 300ml/G;
Application 1: Fire Resistant, EPS Foam, PU Foam;
Application 2: Fireproof Door;
Application 3: Graphite Sheet;
Application 4: Metallurgy,Machinery;
Delivery Time: Within 2 Weeks;
Sample: Free;
|
Type: Flake Graphite;
Composition: C;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Expanded Graphite;
Crystal Morphology: Flake Graphite;
Melting Point: 3250 Degree;
pH: 6-7;
Ash: 5-10%;
80 Mesh: Over 75%;
Color: Black, Sliver Grey;
Fixed Carbon: 90-99%;
Expandable Rate: 180ml/G - 300ml/G;
Application 1: Fire Resistant, EPS Foam, PU Foam;
Application 2: Fireproof Door;
Application 3: Graphite Sheet;
Application 4: Metallurgy,Machinery;
Delivery Time: Within 2 Weeks;
Sample: Free;
|
Type: Graphite Electrodes;
Composition: Coke, Pitch, Needle Coke;
Carbon Content: High-Carbon;
Grade: HP;
Forming Way: Extruded Graphite;
Crystal Morphology: Aphanitic Graphite;
Product Name: Graphite Electrode;
Bulk Density: 1.65;
Resistivity: 6.5;
Flexural Strength: 9.8-10.5;
Elastic Modulus: 12;
Ash: 0.3;
Cte: 2.4;
|
Type: Graphite Electrode Powder;
Composition: Pet Coke, Pitch, Needle Coke;
Carbon Content: High-Carbon;
Grade: UHP;
Forming Way: Extruded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
|