Specification |
Usage: Filter Material, High Temperature Insulating Material, Gasket;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Paper;
Kind: Ordinary Ceramic Fiber;
Province: Shandong;
Raw Material: Aluminum Silicate Fiber;
Product: Aluminum Silicate Paper;
Name: Ceramic Fiber Paper;
Product Name: Ceramic Fiber;
Manufacturer: Luyang;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Rockwool Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Rockwool;
Bulk Density: 60-200kg/M3;
Thermal Conductivity: 0.044W/M.K @70c;
Shot Content: 12%;
Fiber Mean Value: 7um;
Water Content: 0.5%;
Combustibility: A Grade Nonflammable;
Organic Content: 4.0%;
Hydrophobicity: 98%;
Water Absorption: 5%;
|
Usage: High Temperature Insulating Material;
Chemical Composition:: Al2O3.SiO2;
Manufacturing Technique: Spray Silk Rug;
Bulk Density: 60-200kg/M3;
Thermal Conductivity: 0.044W/M.K @70c;
Shot Content: 12%;
Fiber Mean Value: 7um;
Water Content: 0.5%;
Combustibility: A Grade Nonflammable;
Organic Content: 4.0%;
Hydrophobicity: 98%;
Water Absorption: 5%;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃, 1430;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1350;
Bulk Density(g/cm3): 96-160;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.06;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1260℃, 1430;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430/1600;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1500;
Bulk Density(g/cm3): 64-160;96/128;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.08;
|