Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, High Temperature Insulating Material, Petrochemical;Metallurgy;Power Plant;Furnace;
Temprature Classification: 1900℃, 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Soluble Fiber Blanket;
Kind: High Purity Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050~1600 C.Degree;
Chemical Composition:: Al2O3+Sio2≥99%;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Ceramic Fiber Bulk Wool;
Kind: Ordinary Ceramic Fiber;
Thickness: 6mm-50mm, 1", 1/2"2";
Ultimate Strength (≥ MPa): 0.5MPa (25mm Thickness);
Fiber Diameter: 3-5μm;
Thermal Conductivity: 0.06-0.12;
Classification Temperature: 1200;
Ttensile Strenghth(_Kpa): 30/50/70;
Width: 100mm-1220mm;
Shrinkage (1800 ºF, 3h): 1050~1600 C.Degree;
Density (Kg/M³ ): 128;
Al2O3: ≥43;
Zro2: ≥54;
Permanent Linear Shrinkage: 1000c*24HS2.5;
Density: 64/96/128;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃, 1430;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1350;
Bulk Density(g/cm3): 96-160;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.06;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material;
Temprature Classification: 1900℃, 1600℃, 1500℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Fiber Granules;
Manufacturing Technique: Jilt Silk Rug;
Kind: Ordinary Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Cone;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Into Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|