| Specification |
Usage: High Temperature Insulating Material, Thermal Insulation Material;
Temprature Classification: 1600℃, 1500℃, 1650;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Bloc;
Kind: Alumina Fiber;
|
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1050℃, 1050ºC - 1600ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2;
Shape: Board, Panel, Block;
Manufacturing Technique: Wet Forming Process;
Kind: High Purity Ceramic Fiber;
Grade: Std 1260;
Color: Pure White;
Density: 280-320 Kg/M3;
Compressive Strength: 0.3 MPa;
Loss of Ignition: ≤6;
Regular Size: 1200 * 1000, 1000 * 600, 900 * 600;
Regular Thicknesses: 3 - 100 mm Available;
Special Size: Can Be Customzied;
Features: Excellent Thermal Shock Resistance, Easy to Cut, H;
Application: Back up Insulations for Brick and Monolithic Refra;
OEM: Yes;
|
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1260 - 1600ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2 ,Cr2o3;
Shape: Module, Z-Block;
Manufacturing Technique: Folded by Needle Blanket and Anchor;
Kind: High Purity Ceramic Fiber;
Regular Size: 305 X 305mm;
Thickness Available: 100 to 305 mm;
Special Size: Can Be Customized;
Density: 160 192 ,210 ,230 Kg/M3;
Feature: Faster Insulation ,Low Heat Storage;
Application: High Temperature Furnace ,Kiln and Heater Linings;
H.S.Code: 68061010;
|
Usage: Fireproof & Insulation;
Temprature Classification: 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: High Temperature Melting;
Kind: Conton;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fiber Blanket;
Application: Furnace Insulation Material;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|