Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 16%;
Tsr 950ºC: 100 Cycle;
Rul: 1700ºC;
CCS MPa: 60;
MGO: 85-87;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Sio2;
Product Name: Acid Resistant Brick;
Density: 2.3-2.4G/Cm3;
Sio2: 75%;
Al2O3: 14%;
Anti-Acid: 99.8%;
Water Absorption: 0.2%;
Apparent Porosity: 11%;
Application: Chemical Industry Product;
Sample: Available;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Crucible;
Material: Boron Nitride;
Color: White;
Features: High Temperature Resistant;
Size: Customize;
Delivery Time: 3-30 Days;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Square, Circular, Triangular, etc;
Material: Mullite, Cordierite, High Alumina, etc;
Size: 50*50, 40*40, 65*65, 50*75, etc;
Hole: Square, Circular, Triangular, Hexagonal, etc;
Holes: 100cpsi, 200cpsi, 300cpsi, etc;
Temperature Resistance: 1350-1650celsius Degree;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Powder;
Material: Castable;
Size: 3-5um;
Alumina Content: 99.5%;
Density: 3.95g/Cc;
|