| Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.1-2.2g/cm3;
Apparent Porosity: 16%;
Tsr 950ºC: 16cycle;
Rul: 1300;
CCS MPa: 57;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials, Instant Materials, Hot Products;
Type: Refractory Material;
Shape: Ball;
Material: Alumina Block;
Product Name: High Alumina Refractory Ball;
Sio2 Content (%): 50%~65%;
Al2O3 Content (%): 65%~95%;
MGO Content (%): 0.8-1.2;
Cao Content (%): 0.34%;
Refractoriness (Degree): Super-Class (Refractorines;
Cro Content (%): 0.002%;
Sic Content (%): 1.2-1.4;
Model Number: Refractory Balls, Customer's Requirem;
Cold Crushing Strength(MPa): 13~36;
Application: Insulation Furnace;
Bulk Density(g/cm3): 2.3~3.1;
Size(mm): 40-80mm;
Apparent Porosity(%): 25~18;
Thermal Shock Resistance: 7~20;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Type: Refractory Material;
Shape: Round, Square, Oval, Half Tube;
Surface Finish: Polished, Glazed, Metalized;
Optional Material: Zirconia, Silicon Nitride, Aluminum Nitride;
Precision Tolerance: Od to Be +/-0.005, ID to Be +/-0.01mm;
Product Name: Ceramic Tubes;
Forming Methods: Extrusion, ISO Pressed, Dry Pressed;
Purity of Material: Range From 40% to 99.8%;
Color: White, Ivory, Pink, Black;
Density: Over 3.65g/cm3;
Norminal Tolerance: 1% of Dimensions;
Features: Wear Resistance, Insulation;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Product Name: Fire Clay Insulation Brick;
Fe2o3: Less Than 2%;
Cold Crushing Strength MPa: More Than 1.5-6;
Crushing Strength: 40~60 MPa;
Apparent Porosity: 40-80%;
Max Service Temperature °c: 1150-1400c;
Bulk Density(g/cm3): 0.55-1.5;
Color: Yellow;
Application: Industrial Furnaces;
Brick Feature: Excellent Thermal Shock Resistance;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Product Name: Fire Clay Insulation Brick;
Fe2o3: Less Than 2%;
Cold Crushing Strength MPa: More Than 1.5-6;
Crushing Strength: 40~60 MPa;
Apparent Porosity: 40-80%;
Max Service Temperature °c: 1150-1400c;
Bulk Density(g/cm3): 0.55-1.5;
Color: Yellow;
Application: Industrial Furnaces;
Brick Feature: Excellent Thermal Shock Resistance;
|