Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Mullite;
Application Area: Transition zone and safety zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.67-2.7g/cm3;
Apparent Porosity: 17%;
Tsr 1100ºC: 10 Cycle;
Rul: 1680ºC;
CCS MPa: 90;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Lumo,Granule,Briquette,Powder;
Material: Silicon Carbide (SiC);
Application: Refractory;
Usage: Metallurgy;
Color: Black;
Chemical Composition: Sic;
|
Classification: Sintered Magnesia Brick;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Feature: Long Time Materials;
Type: Refractory Material;
Material: MGO-Carbon Brick;
Sio2: 1%~3.5%;
MGO: 92%-95%;
Application Limit Temp: 1800c;
Cold Crushing Strength: 55~80MPa;
Thermail Shock Resistance @950c: 10;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Roll, Ceramic Fiber Blanket;
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1260℃, 1430;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430/1600;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1500;
Bulk Density(g/cm3): 64-160;96/128;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.08;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Block;
Material: Alumina Block;
Brand: Hitech;
Zro2: 20%;
Al2O3: 58%-66%;
Fe2o3: 0.5%;
Bulk Density: 3.0g/cm3;
Apparent Porosity: 15%;
Cold Crushing Strength: 110MPa-140MPa;
Refractoriness Under Load: 1650c;
|