Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Powder;
Material: Fly Ash;
Name: Cenosphere;
Size: Ball;
Al2O3 Content (%): 33-38;
Sio2: 56-62%;
Fe2o3: 2-4%;
Cao: 0.2-0.4%;
MGO: 0.8-1.2%;
K2o: 0.5-1.1%;
Na2o: 0.3-0.9%;
Mesh: 20-40, 30-60,40-70,70-100;
Refractoriness: 1770°< Refractoriness< 2000°;
Color: Grey;
Sample: Free;
Quality: Top;
MSDS: Yes;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Andalusite;
Application Area: Transition zone and safety zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.67-2.7g/cm3;
Apparent Porosity: 17%;
Tsr 1100ºC: 10 Cycle;
Rul: 1680ºC;
CCS MPa: 90;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: burning and transition Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 16%;
Tsr 950ºC: 100 Cycle;
Rul: 1700ºC;
CCS MPa: 60;
MGO: 85-87;
Standard: VDZ/ISO;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 7-9%;
Cold Crushing Strength: 45-55MPa;
Refractoriness Under Load: 1550-1700;
Al2O3: 65-72%;
Sic: 10-11%;
FC: 10-13%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35,Sk36,Sk37,Sk38,Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|