Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Brick;
Material: Aluminum/Silicon Carbide/Zircornia/Cordierite;
Hole Shape: Square / Round / Hexagon/Triangle;
Size: 50*50*20mm, 65*65*15mm, 100*75*13mm, 81*12mm;
Outer Shape: Square, Rectangle, Round;
Working Temp.: ≤1500 Degree;
Hole Number: 100/200/300csi;
Hole Rate: 35-60%;
Bending Strength: ≥1MPa (at Normal Temperature);
Compressive Strength: ≥20MPa (at Normal Temperature);
Volume Density: 0.8-1.2g/cm3;
Customization: Yes;
|
Feature: Long Time Materials;
Type: Magnesium Oxide Boards;
Color: White, Grey, Red, Green;
Density: 1.0-1.2g/cm3(GB/T-7019-1997);
Fire Ratings: A1 Grade (GB 8624);
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Brick;
Material: Alumina Cement;
Al2O3: 92% 95%;
Color: White;
Size: 150X100X6-26mm;
Density: 3.65g/cm3;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Cement;
Al2O3: 92% 95%;
Color: White;
Density: 3.65g/cm3;
Size: 150X100X6-25mm;
Hardness: 9 Mohs;
Sample: Free;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Materials: 92% Al2O3 or 95% Al2O3;
Density: 3.60 or 3.68;
Moh's: 9;
Industry: Mining, Steel Plant, Power Plant, etc;
Facility: Hopper, Bunker, Stacker, Chute, Pipe;
OEM: Acceptable;
Sample: Available;
Size: 150X150mm;
Grade Standard: Industrial Grade;
Quality: First Class;
|