| Specification |
Application: Industrial Ceramic, Alumina Ceramic;
Type: Ceramic Plates;
Useful: Aluminium Filtrate;
Material: Alumina Ceramic;
|
Application: Refractory, Structure Ceramic, Industrial Ceramic, Functional Ceramic;
Type: Ceramic Plates;
Forming Method: Tape Casting;
Features: High Mechanical Strength, Small Dielectric Loss;
Optional Color: White, Ivory, Pink, Black;
Density: Over 3.70g/cm3;
Standard Thickness: 0.2-2.0mm Available;
Thickness Tolerance: ±0.03/0.05mm (Depending on Thickness);
Length and Width Tolerance: ±2mm;
Material: Alumina Ceramic;
|
Application: Refractory, Industrial Ceramic;
Type: Ceramic Plates;
Standard: GB, ISO;
Item: Wear Resistant Alumina Lining Pieces;
Alumina Content: 92% Al2O3, 95% Al2O3, Zta;
Density: 3.60-4.20g/Cc;
Property: High Hardness/Purity/Wear Resistant/Wear Impact;
Compressive Strength: 850~1000MPa;
Mat: Paper/Silk/Net/Rubber;
Size: Available and Customized Size;
Applied Equipment: Chute, Hopper, Silo, Bunker, Funnel, Conveyer;
Material: Alumina Ceramic;
|
Application: Refractory, Industrial Ceramic;
Type: Ceramic Parts;
Product Name: Rto/Rco Honeycomb Ceramics;
Shape: Three-Dimensional Network Connected;
Thermal Expansion Coefficient: <2;
Characteristic: Long Service Life;
Size: Customizable;
Attribute: High Temperature Resistance;
Usage: Melting Aluminium, Copper;
Keyword: Honeycomb Ceramic Regenerator;
Feature: High Thermal Conductivity, Acid and Alkali;
Specific Heat: 830-900;
OEM: Yes;
Heat Transfer Area: 390-800;
Porosity: 30%-90%;
Apparent Porosity: 5~18%;
Material: Alumina Ceramic;
|
Application: Industrial Ceramic;
Purity: 95%;
Type: Ceramic Plates;
Al2O3(%): 92%;
Density: 3.6g/cm3;
Bending Strength(MPa): 220;
Fracture Toughness(MPa.M1/2): 3.2;
Rockwell Hardness Hra: 82;
Vickers Hardness Hv20(MPa): 950;
Wear Volume(Cm³): 0.25;
Hv 20: 950;
Color: White;
Material: Alumina Ceramic;
|