Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Wet Forming Process;
Kind: High Purity Ceramic Fiber;
Item: Ceramic Fiber Board;
Temperature: 1050-1600 ºC;
Density: 280/300/320/350/400/450 Kg/M3;
Color: White/ Pure White;
Al203+Sio2: 97-99 %;
Application: Heat Insulation;
Refractory Grade: Non-Inflammable;
Melting Point: 1760 ºC;
Thickness: 6mm-50mm Thickness;
Width: 500/600/1000 mm or Customized;
Length: 900/1000/1200 mm or Customized;
Raw Material: Ceramic Fiber Bulk;
Type: Heat-Resistant Material;
Grade: Std/HP/Ha/Hz;
Performance: Excellent;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|