Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Textile;
Kind: Ordinary Ceramic Fiber;
Warranty: 12 Months;
MOQ: 1PC;
Asbestos: 100% Non Asbestos;
Thickness: 1.6-6.4mm;
Function: Insulation, Sealing and Filling;
Raw Materials: Spuned Ceramic Fiber Bulk;
Product: Ceramic Fiber Tape;
Density: 500±15 Kg/M³;
Product Type: Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃, 1350ºC;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Al2O3+Sio3: 96%;
Al2O3: 43%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 320kg/M3;
Specific Heat Capacity(: 0.8kj/Kg.K;
Compressive Strength: 0.3MPa;
Linear Shrinkage(800ºC): 2.0%;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|