Specification |
Shape: Conical, Circular, Cylindrical;
Color: White, Light Yellow;
Refractoriness: 1580< Refractoriness< 1770;
Type: Ceramic Crucible;
Name: Clay Pot Clay Crucible for Laboratory Testing;
Max. Working Temperature: 1380 Degree Celsius;
Item: Ceramic Crucible;
Application: Thermal Analysis or Firing;
Capacity: 10ml, 20ml, 30ml, 50ml, 80ml, 100ml, 200ml, 500ml;
Feature: Long Time Materials, Instant Materials;
Material: Clay;
Purpose: Gold Smelting and Assaying;
Size: 30g,40g,45g,50g,65g,Others;
Usage: Melting,Assaying;
Refractoriness Under Load: 1420 Degree Celsius;
Packing: Wooden Packing,Paper Carton Packing;
|
Shape: Cylindrical, Cylindrical;
Color: Black, Black;
Refractoriness: 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Type: Graphite Crucible, Silicon Carbide Crucible;
Composition: Sic;
Carbon Content: Medium-Carbon;
Grade: Industrial Grade;
Forming Way: Isostatic Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Chemical Content: C: 37-42% Sic: 35-40%;
Apparent Porosity: 9-12%;
Stock: Should Be Stocked in The Dry Situation;
Application: Non-Metal Melting/Induction Furnace;
|
Shape: Cylindrical, Cylindrical;
Color: Black, Black;
Refractoriness: 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Type: Graphite Crucible, Silicon Carbide Crucible;
Composition: Sic;
Carbon Content: Medium-Carbon;
Grade: Industrial Grade;
Forming Way: Isostatic Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Chemical Content: C: 37-42% Sic: 35-40%;
Apparent Porosity: 9-12%;
Stock: Should Be Stocked in The Dry Situation;
Application: Non-Metal Melting/Induction Furnace;
|
Shape: Cylindrical, Cylindrical;
Color: Black, Black;
Refractoriness: 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Type: Graphite Crucible, Silicon Carbide Crucible;
Composition: Sic;
Carbon Content: Medium-Carbon;
Grade: Industrial Grade;
Forming Way: Isostatic Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Chemical Content: C: 37-42% Sic: 35-40%;
Apparent Porosity: 9-12%;
Stock: Should Be Stocked in The Dry Situation;
Application: Non-Metal Melting/Induction Furnace;
|
Shape: Cylindrical, Cylindrical;
Color: Black, Black;
Refractoriness: 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Type: Graphite Crucible, Graphite Crucible;
Material: Clay Graphite;
Application: Metal Melting/Refining Furnace;
Apparent Porosity: ≤23%;
Bulk Density: ≥1.75g/Cm³;
Composition: Clay;
Carbon Content: Medium-Carbon;
Grade: Industrial Grade;
Forming Way: Molded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
|