Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 78%;
Alloy: Alloy;
Type: Nickel Pipe;
Powder: Not Powder;
Material: Alloy Steel;
Grade: Hastelloy, Inconel, Monel;
Standrad: ASTM, GB, DIN, AISI, JIS, BS;
Hastelloy: B3/B2/X/C/C22/C276/G-30/N/X;
Special Application: Ships, Molds, Aerospace Equipment, Chemis;
Surface: Polished/ Galvanized/Coated/Color Coated;
Inconel: 600/601/625/718/750/X-750/800;
Edges: Mill Edge, Slit Edge;
Monel: 400/K500/404;
Technical: Hot Rolled/Cold Rolled;
Tolerance: 1%, 2%, 3%, Customize;
Size: 4X8FT/5X10FT/Customize;
Sample: Free;
MOQ: 1 Ton;
Price Term: CIF CFR Fob Ex-Work;
|
Application: Electronics, Industrial, Medical, Chemical;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Powder;
Powder: Powder;
Appearance: Greyish Powder;
CAS No.: 7440-02-0;
Particle Size(μm): 3-10μm or 3-8μm;
D50(μm): 10-11 or 5-6;
Screen Analysis (Mesh): 450 or 635;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: 78%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Density: 8.4;
Elongation: 20;
Sample: Free;
Max Continuous: 1200;
Technique: Cold Drawing;
Treatment: Hydrogen Annealing;
Surface: Bright;
Condition: Soft Annealed;
Tensile: 630~780;
Resistivity: 1.09+/5% Ohm/M;
Spool: DIN80 DIN100 DIN125;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: 30-46%;
Alloy: Alloy;
Type: Nickel Bar;
Powder: Not Powder;
Grade: Incoloy 800 800h 800ht 825 925;
MOQ: 20kg;
Surface: Bright, Oxidized Color, Acid White;
Density: 8.19 G/Cm³;
Dilatation Coefficient: 13.0 μm/M °c;
Melting Point: 1336;
Treatment: Hydrogen Annealing;
Elongation: 30%~46%;
Ultimate Strength: 462MPa;
Types: Wire Sheet Bar Plate Foil Pipe;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: >99.95%;
Alloy: Non-alloy;
Type: Nickel Bar;
Powder: Not Powder;
Melting Point: 1357-1385;
Shape: Wrie, Pipe, Bar, Strip, Plate;
Surface: Bright;
Technique: Cold Treatment;
Manufacturing Process: Solution Treatment;
Tensile Strength: 950 N/mm2;
Yield Strength: 546 N/mm2;
Elogation: 35%;
|