Specification |
Material: EVA;
Kind: Color Plastic Sheet;
Water Absorption: 0.2%~0.3%;
Contraction Percentage: <0.4%;
Tensile Strength: 30~40MPa;
Hardness: 20- 80 Degree(Shore C);
Use: Shoe Material, Sport Products;
Features: Resiliency, Excellent Buoyancy, Shock Absorption;
Environmental: Yes;
|
Material: PVC;
Kind: White Plastic Sheet;
Water Absorption: 0.12%~0.25%;
Contraction Percentage: <0.4%;
Tensile Strength: 51~80MPa;
Width: 1.22, 2.05;
Length: 2.44, 3.05;
Thickness: Thickness;
Density: 0.45-1.0;
Hardness: 50-80;
Impact Strength: 10-18;
Vicat Softening Point: 75-80;
Water Absorbing Rate: <1.2;
Self Extinguishing Level: <5 Seconds;
Min. Order: Min. Order;
|
After-sales Service: If Any Problem, Please Feel Free to Let Us Know;
Warranty: 3-5 Years;
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: 0.2%~0.3%;
Contraction Percentage: <0.4%;
Tensile Strength: 51~80MPa;
Size: 1220*2440mm;
Density: 0.5380.8;
Thickness: 1-50mm;
Color: White or Color;
Surface: Glossy / Matt;
Application: Advertisement, Furniture, Engraving, Building;
|
After-sales Service: One Year;
Warranty: One Year;
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: 0.2%~0.4%;
Contraction Percentage: 0.4%~1.4%;
Tensile Strength: 30~40MPa;
Product Name: PVC Foam Board;
Density: 0.3-0.9g/cm3;
Color: White, Black, Colorful;
Thickness: 1-30mm;
Brand Name: Gokai;
Process Type: Free, Celuka, Co-Extrusion;
Surface: Matte / Glossy;
Samples: Free and Any Time;
Other: Support Secondary Process;
|
Material: Acrylic;
Kind: Transparent Plastic Sheet;
Water Absorption: 0.1%~0.3%;
Contraction Percentage: <0.4%;
Tensile Strength: 30~40MPa;
Products Name: Acrylic Sheet/PMMA(Plexiglass);
Sheet Type: Cast Acrylic/Extrusion Acrylic;
Thickness: 2-30mm;
Size: 1.22 X 2.44m/2.05 X 3.05m;
Density: 1.2g/cm3;
Raw Material Grade: 100% Virgin Raw Material;
Color: Transparent/Clear, Colored for Choose;
Light Transmission: >92% for 100% Virgin Raw Material;
Application: Engraving Display, Kitchen & Bathroom Furniture;
Product Name: Acrylic Sheet/Plexiglass Sheets(PMMA);
|