| Specification |
Material: Stainless Steel;
Type: A2 A4;
Connection: Common Bolt;
Head Style: Hexagonal;
Standard: DIN, ANSI, GB, JIS, BSW;
Grade: 304 316;
Application: Building;
Packing1: Bulk;
Packing2: Small Box;
Packing3: Plastc Bucket;
Material 1: Ss 304;
Material 2: Ss 316;
Material 3: Ss 201;
Material 4: Ss 410;
Delivery Time: 20 to 40 Days;
|
Material: Carbon Steel;
Type: Hexagon Head With Flange;
Connection: Common Bolt;
Head Style: Flange Head;
Standard: DIN, ANSI, GB, JIS, BSW, Non-Standard;
Grade: High Tensile;
Application: Machinery, Chemical Industry, Environmental, Building, Automotive Industry;
Finish: Color-Zinc Plated;
Thread: Metric or Inch;
Thread Type: Fine / Coarse /Bsw/Bsf/ Unc/Unf;
8.8 Hardness: HRC 22-32;
8.8 Tensile Strength: Above 800 MPa;
8.8 Yield Strength: Above 640 MPa;
10.9 Hardness: HRC 33-38;
10.9 Tensile Strength: Above 1040 MPa;
10.9 Yield Strength: Above 940 MPa;
12.9 Hardness: HRC 39-45;
12.9 Tensile Strength: Above 1200MPa;
|
Material: High Strength Steel;
Type: Hexagon Head With Flange;
Connection: Common Bolt;
Head Style: Flange Head;
Standard: DIN, ANSI, GB, JIS, BSW, Non-Standard;
Grade: 8.8;
Application: Machinery, Chemical Industry, Environmental, Building, Automotive Industry;
Finish: Color-Zinc Plated;
Thread: Metric or Inch;
Thread Type: Fine / Coarse /Bsw/Bsf/ Unc/Unf;
8.8 Hardness: HRC 22-32;
8.8 Tensile Strength: Above 800 MPa;
8.8 Yield Strength: Above 640 MPa;
10.9 Hardness: HRC 33-38;
10.9 Tensile Strength: Above 1040 MPa;
10.9 Yield Strength: Above 940 MPa;
12.9 Hardness: HRC 39-45;
12.9 Tensile Strength: Above 1200MPa;
|
Material: High Strength Steel;
Type: Hexagon Head With Flange;
Connection: Common Bolt;
Head Style: Flange Head;
Standard: DIN, ANSI, GB, JIS, BSW, Non-Standard;
Grade: 8.8;
Application: Machinery, Chemical Industry, Environmental, Building, Automotive Industry;
Finish: Color-Zinc Plated;
Thread: Metric or Inch;
Thread Type: Fine / Coarse /Bsw/Bsf/ Unc/Unf;
8.8 Hardness: HRC 22-32;
8.8 Tensile Strength: Above 800 MPa;
8.8 Yield Strength: Above 640 MPa;
10.9 Hardness: HRC 33-38;
10.9 Tensile Strength: Above 1040 MPa;
10.9 Yield Strength: Above 940 MPa;
12.9 Hardness: HRC 39-45;
12.9 Tensile Strength: Above 1200MPa;
|
Material: High Strength Steel;
Type: Hexagon Head With Flange;
Connection: Common Bolt;
Head Style: Flange Head;
Standard: DIN, ANSI, GB, JIS, BSW, Non-Standard;
Grade: 8.8;
Application: Machinery, Chemical Industry, Environmental, Building, Automotive Industry;
Finish: Color-Zinc Plated;
Thread: Metric or Inch;
Thread Type: Fine / Coarse /Bsw/Bsf/ Unc/Unf;
8.8 Hardness: HRC 22-32;
8.8 Tensile Strength: Above 800 MPa;
8.8 Yield Strength: Above 640 MPa;
10.9 Hardness: HRC 33-38;
10.9 Tensile Strength: Above 1040 MPa;
10.9 Yield Strength: Above 940 MPa;
12.9 Hardness: HRC 39-45;
12.9 Tensile Strength: Above 1200MPa;
|