Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: Ni (Min)35-38%;
Alloy: Alloy;
Type: Nickel Pipe;
Powder: Not Powder;
Surface: Bright;
Density: 8.1G/M3;
Melting Point: 1430;
Technique: Cold Drawing;
Treatment: Hydrogen Annealing;
Condition: Soft Annealed;
MOQ: 1kg;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.55;
Density: 8.6cm3;
Curie Point: 450 C;
Saturation Magnetostriction Coefficient: 2;
Hardness: 120~210 Hv;
Tensile Strength: 560~1030 MPa;
Yield Strength: 150~980 MPa;
Elongation: 3~50 %;
Use: High Frequency Inductive Components;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.55;
Density: 8.6cm3;
Curie Point: 450 C;
Saturation Magnetostriction Coefficient: 2;
Hardness: 120~210 Hv;
Tensile Strength: 560~1030 MPa;
Yield Strength: 150~980 MPa;
Elongation: 3~50 %;
Use: High Frequency Inductive Components;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.55;
Density: 8.6cm3;
Curie Point: 450 C;
Saturation Magnetostriction Coefficient: 2;
Hardness: 120~210 Hv;
Tensile Strength: 560~1030 MPa;
Yield Strength: 150~980 MPa;
Elongation: 3~50 %;
Use: High Frequency Inductive Components;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.55;
Density: 8.6cm3;
Curie Point: 450 C;
Saturation Magnetostriction Coefficient: 2;
Hardness: 120~210 Hv;
Tensile Strength: 560~1030 MPa;
Yield Strength: 150~980 MPa;
Elongation: 3~50 %;
Use: High Frequency Inductive Components;
|