| Specification |
Material: Steel;
Content: >90%;
Usage: Machinery, Chemical, Grind, Cement Plant Power Industry;
Processing Type: Forging, Rolling, Casting;
Size: 20mm-150mm;
Color: Black;
Customized: Customized;
Breakage Rate: <1%;
Loss Roundness Rate: <1%;
Application: Ball Mill, Sag Mills, Vertimills, Mineral Process;
Hardness: 60-65HRC;
Service: Free Samples;
Impact Toughness: >12ak.J/Cm2;
|
Material: Alumina;
Content: >90%;
Usage: Machinery, Chemical, Petroleum, Grind, Refractory Material, Ceramic Body and Glaze, Mineral Powder, Paint,etc.;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Item: Alumina Ceramic Grinding Balls/Beads;
Function: Grinding and Dispersing;
Density: 3.6~3.7g/cm3;
Moh's Hardness: 9;
Application Industry: Mining,Metallurgy,Glass,Porcelain Enamel,Pigment;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|