Specification |
Refractoriness (℃): 1650;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Cylinder;
Material: Ceramic Fiber;
Inner Size: 13.5*4.5cm;
Weight: 1kg;
Manufacturing Process: Cementation;
Color: White;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: Clay, Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method, Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 35%~45%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk32-34;
Apparent Porosity: 13-26%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1250-1500;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-3.0%;
|
Feature: Long Time Materials;
Type: Mitten, Finger;
Material: Ceramic Fiber Yarn;
Width: 610mm-1220mm, 610mm/1220mm;
Length: 60m, 50m, 15m or Any Length, 20m/30m/40m;
Thickness: 2mm-10mm;
Color: White;
Temperature: 1350c;
Shrinkage (1800ºF, 3h): -3(24hours);
Density (Kg/M³ ): 160;
Thermal Conductivity: 0.075;
Fiber Diameter: 3-5um;
Ultimate Strength (≥ MPa): 0.08;
Grade: St (Standard);
|
Production Process: Fusion Method;
Refractoriness (℃): Refractoriness> 2000;
Shape: Grit / Powder/ Grain / Sand;
Chemical Al2O3: Min: 99.2%;
Advantage: Manufacturer, Can Be Customized;
Color: White;
Volume Density: 3.6g/cm3;
|