Specification |
Grade: Grade A;
Thickness: 3mm;
Appearance: Customized;
Color: Customized;
Material: Kraft and Melamine Paper;
Type: High Pressure Laminate;
Surface Finishing: Special;
Edge: Square;
Shape: Rectangle;
Usage: Furniture, Building, Cabinet Countertops,Cabine Doors,Kitchen;
|
Grade: Grade A;
Thickness: 10mm;
Appearance: Panel;
Color: Gray White;
Material: Non-asbestos;
Type: Fibre Board;
Surface Finishing: Glossy;
Edge: Tapered;
Shape: Square;
Refractory Temperature: Over 2000 ℃;
Usage: Building;
Length: 2400, 2440, 3000;
Width: 1200, 1220;
Fire-Proof Rate: a-Class Incombustible(GB8624-1997);
Incombustibility(Min): 240minutes;
Density: 1.2-1.4G/Cm3;
Water Content Ratio: ≤10%;
Swelling Ratio: ≤0.20%;
Anti-Bending Strength: ≥12MPa;
|
Grade: Grade A;
Thickness: 10mm;
Appearance: Panel;
Color: Gray White;
Material: Non-asbestos;
Type: Fibre Board;
Surface Finishing: Glossy;
Edge: Tapered;
Shape: Square;
Refractory Temperature: Over 2000 ℃;
Usage: Building;
Length: 2400, 2440, 3000;
Width: 1200, 1220;
Fire-Proof Rate: a-Class Incombustible(GB8624-1997);
Incombustibility(Min): 240minutes;
Density: 1.2-1.4G/Cm3;
Water Content Ratio: ≤10%;
Swelling Ratio: ≤0.20%;
Anti-Bending Strength: ≥12MPa;
|
Grade: Grade A;
Thickness: 10mm;
Appearance: Panel;
Color: Gray White;
Material: Non-asbestos;
Type: Fibre Board;
Surface Finishing: Glossy;
Edge: Tapered;
Shape: Square;
Refractory Temperature: Over 2000 ℃;
Usage: Building;
Length: 2400, 2440, 3000;
Width: 1200, 1220;
Fire-Proof Rate: a-Class Incombustible(GB8624-1997);
Incombustibility(Min): 240minutes;
Density: 1.2-1.4G/Cm3;
Water Content Ratio: ≤10%;
Swelling Ratio: ≤0.20%;
Anti-Bending Strength: ≥12MPa;
|
Grade: Grade A;
Thickness: 10mm;
Appearance: Panel;
Color: Gray White;
Material: Non-asbestos;
Type: Fibre Board;
Surface Finishing: Glossy;
Edge: Tapered;
Shape: Square;
Refractory Temperature: Over 2000 ℃;
Usage: Building;
Length: 2400, 2440, 3000;
Width: 1200, 1220;
Fire-Proof Rate: a-Class Incombustible(GB8624-1997);
Incombustibility(Min): 240minutes;
Density: 1.2-1.4G/Cm3;
Water Content Ratio: ≤10%;
Swelling Ratio: ≤0.20%;
Anti-Bending Strength: ≥12MPa;
|