Specification |
Refractoriness (℃): 1380;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Color: Black;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Alumina;
Alumina Content: 60-80%;
Size: Od 8-50;
Color: White, Pink Cream;
End: Oec or Beo;
Application: High Temperature Resistant, High Wear Resistance;
Finish: Collar, Slot, Curve;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|