Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Square, Circular, Triangular, etc;
Material: Mullite, Cordierite, High Alumina, etc;
Size: 50*50, 40*40, 65*65, 50*75, etc;
Condition: Square, Circular, Triangular, Hexagonal, etc;
Holes: 100cpsi, 200cpsi, 300cpsi, etc;
Color: White;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Mullite;
Sio2 Content: 34%;
Al2O3 Content (%): 65%;
MGO Content (%): <=0.5%;
Refractoriness (Degree): 1300~1630;
Cro Content (%): 0.1~0.3%;
Standard Size: 230*114*65mm;
Application: Hot Surface and Back-up Lining of Industrial Furna;
Fe2o3 %: 1.0;
Apparent Porosity %: 20;
Bulk Density g/cm3: 0.6,0.8,1.0,1.2;
Name: Mullite Insulation Brick;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Heat-Resistant Material;
Material: Alumina Cement;
Thickness: 6-50mm;
Width: 610/1220mm;
Length: 7200mm or Your Requirment;
Chemical Composition: Al2O3+Sio2≥99%;
Ultimate Strength (≥ MPa): 0.08-0.12;
Fiber Diameter: 3-5μm;
Application: Refractory Furnace Lining Insulation Materials;
Density (Kg/M³ ): 128;
Feature 1: Low Thermal Conductivity,Low Heat Storage;
Feature 2: Good Thermal Shock Resistance;
Feature 3: Reasonable Price;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Mullite;
Sio2 Content: 34%;
Al2O3 Content (%): 65%;
MGO Content (%): <=0.5%;
Refractoriness (Degree): 1300~1630;
Cro Content (%): 0.1~0.3%;
Standard Size: 230*114*65mm;
Application: Hot Surface and Back-up Lining of Industrial Furna;
Fe2o3 %: 1.0;
Apparent Porosity %: 20;
Bulk Density g/cm3: 0.6,0.8,1.0,1.2;
Name: Mullite Insulation Brick;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Heat-Resistant Material;
Shape: Castable;
Material: Alumina Cement;
Sio2 Content: 18-50%;
Al2O3 Content: 45-85%;
MGO Content: 0.2-1.3%;
Application: Refractory Furnace Lining Insulation Materials;
Density (Kg/M³ ): 2.2-3.15g/cm3;
Feature 1: Low Thermal Conductivity,Low Heat Storage;
Feature 2: Good Thermal Shock Resistance;
Feature 3: Reasonable Price;
|