Specification |
Application: Industrial;
Standard: GB, ASTM;
Purity: >99.5%;
Alloy: Alloy;
Powder: Not Powder;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: 63%;
Alloy: Non-alloy;
Type: Nickel Bar;
Powder: Not Powder;
Melting Point: 1300~1390;
Surface: Bright/Oxidation;
Elongation (A5%): 35;
Tensile Strength: 480MPa;
Yield Strength: 170MPa;
Hb: Min 331;
Density: 8.9g/cm3;
Shape: Wrie, Pipe, Bar, Strip, Plate;
Technique: Cold Treatment;
Manufacturing Process: Solution Treatment;
Size: 10~200mm;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: More Than 63%;
Alloy: Alloy;
Type: Nickel Plate;
Powder: Not Powder;
Melting Point: 1357-1385;
Shape: Wrie, Pipe, Bar, Strip, Plate;
Surface: Bright;
Technique: Cold Treatment;
Manufacturing Process: Solution Treatment;
Tensile Strength: 950 N/mm2;
Yield Strength: 546 N/mm2;
Elogation: 35%;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: >98%;
Alloy: Alloy;
Type: Hastelloy Wire;
Powder: Not Powder;
Technique: Cold Drawing;
Treatment: Hydrogen Annealing;
Surface: Bright;
Condition: Soft Annealed;
Tensile Strength: 790;
Elongation: 40%;
Composition: Ni 57%, Cr21%, Mo13.5% W 3%;
Densiry: 8.9g/Cm;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: 63%;
Alloy: Non-alloy;
Type: Nickel Bar;
Powder: Not Powder;
Melting Point: 1300~1390;
Surface: Bright/Oxidation;
Elongation (A5%): 35;
Tensile Strength: 480MPa;
Yield Strength: 170MPa;
Hb: Min 331;
Density: 8.9g/cm3;
Shape: Wrie, Pipe, Bar, Strip, Plate;
Technique: Cold Treatment;
Manufacturing Process: Solution Treatment;
Size: 10~200mm;
|