Specification |
CAS No.: 9003-39-8;
Formula: (C6h9no)N;
Molecular Principal Chain: Pvp;
Color: White;
Inci: Pvp,Polyvinylpyrrolidone;
Applications: Personal Care;
Storage: Room Temperature;
Solid Content: 95% Min;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 83-96;
Density,g/cm3: 1.07-1.14;
100% Modulus,MPa: 5-10;
300% Modulus,MPa: 10-25;
Tensile Strength,MPa: 30-45;
Tear Strength,MPa: 77-120;
Procesing Temperature,°c: 165-180;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 75-82;
Density,g/cm3: 1.19-1.22;
100% Modulus,MPa: 5-35;
300% Modulus,MPa: 12-43;
Tensile Strength,MPa: 35-60;
Tear Strength,MPa: 100-240;
Procesing Temperature,°c: 165-180;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.10-1.17;
100% Modulus,MPa: 5-22;
300% Modulus,MPa: 9-30;
Tensile Strength,MPa: 20-42;
Tear Strength,MPa: 75-180;
Elongation at Break,%: 350-700;
Tear Strength,Kn/M: 75-180;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.10-1.17;
100% Modulus,MPa: 5-22;
300% Modulus,MPa: 9-30;
Tensile Strength,MPa: 20-42;
Tear Strength,MPa: 75-180;
Elongation at Break,%: 350-700;
Tear Strength,Kn/M: 75-180;
|