Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃, 650ºC;
Chemical Composition:: Calcium, Magnesium, Silicate Chemistry;
Shape: Braid Yarn;
Manufacturing Technique: Spray Silk Rug;
Kind: Bio-Soluble Fiber;
Color: Green;
Fiber Yarn: Soft Resilient Material;
Reinforced Material: Fiberglass or Stainless Steel;
Thermal Shock Resistance: Good;
Features: Light Weight, Low Heat Storage, etc.;
Application: for Bio-Soluble Fiber Cloth/Tape/Sleeving/Rope;
|
Shape: Ceramic Fiber Tape;
Manufacturing Technique: Braid;
Kind: Ordinary Ceramic Fiber;
Refractoriness: 800-1400 °c;
Diameter: 10~750mm;
Color: White;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Packing Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Module;
Kind: Ordinary Ceramic Fiber;
Length: as Per Customer's Request;
Width: as Per Customer's Request;
Thickness: as Per Customer's Request;
Density: 160kg/M3;
Color: White;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Packing Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Length: 3600mm, 7200mm, or Other Customer's Request;
Width: 600mm, 610mm;
Thickness: 10mm~50mm;
Chemical Composition: Al2O3, Sio2;
Density: 96kg/M3 or 128kg/M3 or 160kg/M3;
Color: White;
Fiber Diameter: 3-5um;
Place of Original: Shandong;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1100;
Bulk Density(g/cm3): 64-128;
Linear Shrinkage After Heating: -2.5;
Tensile Strength(MPa): 0.03-0.05;
Sio2: 55-65%;
Cao: 22-35%;
MGO: 5-10%;
Fiber Diameter: 3.5um;
Shot Content: 12%;
|